3D Prism Dental Zirconia Disc
One For All - Isostatically pressed with a lifetime warranty.
Vsmile 3D Prism Multilayer Zirconia Disc 9-layer (4 layers plus 5 transition layers) is a dental multilayer zirconium oxide (4Y-TZP cervical, 5Y-TZP incisal) with natural color and translucency gradient and high flexural strength (1200 MPa cervical, 700 MPa incisal) for anterior- or posterior teeth restorations with up to 14 units. In the production process, 5 layers of pre-colored zirconia are layered on top of each other, building 4 transition layers in the process.The result is an extremely natural color transition for vivid, lively restorations.
Vsmile 3D Prism Multi Layered Zirconia is focused on multilayer ceramic restorations with Vsmile fabrications on esthetic dentistry. The innovative multi-layered technology offering the best possible solution that meets the full arch requirements of the individual clinical esthetic expectation.
Vsmile 3D Prism Multilayer natural appearance of color gradation,based on multilayer technology to ensure a cubic phase inside the zirconia can be fabricated to reduce light birefringence to any kind of tetragonal zirconia polycrystals stabilized with 3mol% Y2O3 zirconia, so translucency can be increased.
Vsmile 3D Prism Multilayer Milling Disc combined the concept of nature and beauty, with smooth color gradation, very matching classical shades as below full arch case shows. Meanwhile the 3D Prism Multilayer physical states can be kept well with our R&D technology to ensure a long-term aesthetic appearance.
Delivery forms
98mm (10mm, 12mm, 14mm, 16mm, 18mm, 20mm, 22mm, 25mm30mm)For Open System
71mm (10mm, 12mm, 14mm, 16mm, 18mm, 20mm, 22mm, 25mm, 30mm)For Amann Girrbach CERAMILL CAD/CAM SYSTEM
95mm (10mm, 12mm, 14mm, 16mm, 18mm, 20mm, 22mm, 25mm, 30mm)For Zirkonzahn CAD/CAM SYSTEM
Colors
A1 A2 A3 A3.5 A4 B1 B2 C1 C2 + Bleach Shades
Packaging
Zirconia Block x 1
Operating Instructionx1
Colors:
Vita 16Shades + Invclar Bleach Shades
Technical parameters:
Chemical component and character
| Y2O3 | Al2O3 | Fe2O3 | Mn2O3 | Accelerated aging | Chemical solubility |
| 4.5-10wt% | 0.05wt% | ≤0.15wt% | ≤0.01wt% | Monoclinic phase＜15% | ≤100μg.cm-3 |
Mechanical property
| Density | Fracture toughness | Hardness(Hv10) |
| ≥6.05g.cm-3 | 5MpaM0.5 | 1250 |
Indications for use:
Veneer, Inlay, Coping, Anterior Full Crown, Posterior Full Crown, Planting Full Crown, Bridge(3 Units) ，Bridge(＞4 Units) ，Coping（3 Units），Coing(＞4 Units).